Technical Properties of Engineering Plastics
Characteristic Method of verification Unit UHMW PE UHMW PE - ESD HMW PE HDPE POM - ESD ABS PA 6 PA 6G PA 6G - OIL FILLED PA 6 - ESD PA 66 PVDF PTFEf PFA PETP PBT U-PVC C-PVC PP PP - GF PEEK PEEK-GF PEEK-CA PAI PPS PPS-GF PES PEI PSU PI PU PC
I. Physical Properties　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　
Density ISO 1183 g/cm3 0.93 0.93 0.95 0.95 1.39 1.06 1.13 1.15 1.15 1.15 1.14 1.79 2.18 2.17 1.37 1.31 1.36 1.55 0.92 1.14 1.30 1.51 1.41 1.42 1.35 1.64 1.37 1.27 1.24 1.43 1.25 1.20
Water absorption ISO 62 % 0.01 0.01 0.01 0.00 0.25 0.40 3.00 2.50 2.50 1.60 2.80 < 0.05 < 0.05 < 0.01 0.25 0.25 0.20 0.20 0.01 0.01 0.10 0.10 0.10 2.50 0.01 0.02 0.70 0.70 0.20 1.30 - 0.35
II. Mechanical Properties　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　
Tensile strength at yield ISO 527-2 MPa 17 17 25 27 45 45 90 80 70 52 90 50 25 28 90 55 55 57 30 - 97 - - 147 75 - 90 105 70 - 49 70
Tensile strength at break ISO 527-2 MPa 40 40 40 35 - - - - - - - 46 - 　 - - 30 80 - 85 - 155 200 137 72 185 6 85 6 86 - -
Elongation at break ISO 527-2 % ≧ 50 > 50 > 50 ≧ 700 ≧ 20 - ≧ 50 3 20 162 40 ≧ 50 > 50 300 15 - ≧ 10 15 ≧ 50 3 25 2.7 1.5 21 21 1.9 40 60 ≧ 50 7.5 600.0 ≧ 50
Modulus of elasticity after tensile test ISO 527-2 MPa 650 650 1,100 1,000 1,400 2,400 3,000 3,300 2,500 - 3,100 2,000 700 700 3,200 2,500 　 　 1,600 5,500 - 9,500 18,500 3,800 3,700 14,000 2,700 3,200 2,600 3,275 - 2,300
Modulus of elasticity after flexural test ISO 178 MPa 800 800 900 1,000 1,450 - - - - - 2,830 2,000 - 670 - - 　 　 - - 4,200 10,000 20,000 3,750 3,600 13,000 - 3,300 - 3,100 - -
Hardness - Rockwell ISO 2039-2 　 - - - - M84 - - - - R93 - - - 　 M95 - - - - - - M99 M102 E79 M100 - M89 - - M119 - -
Hardness - Shore D DIN 53505 　 61 62 62 64 - 70 82 84 83 - 82 78 55 - 60 60 - - 82 90 70 - 88 92 - - - - - 82 86 - 83 85
Charpy impact strength at 23℃ ISO 179 kJ/m2 N. B.? N. B.? N. B.? N. B.? N. B.? N. B.? N. B.? N. B.? - - N. B.? N. B.? N. B.? N. B.? 40.00 N. B.? 　 　 N. B.? 40 N. B.? 60 35 N. B.? 50 45 N. B.? 4 N. B.? 3.50 N. B.? N. B.?
Friction coefficient DIN 53375 　 0.25 0.25 0.29 0.30 0.20 0.50 0.38 0.36 - - 0.35 0.34 0.08 　 0.25 0.24 0.60 0.60 0.30 0.50 0.34 0.42 - - 0.40 0.40 - - 0.40 0.35 0.38 0.50
III. Thermal Properties　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　
Heat deflection temperature - HDT/A ISO 75-2 ℃ 42 - 44 49 105 88 75 95 - 75 85 104 - - 95 80 - - 65 140 152 230 230 280 115 260 200 190 174 360 - 130
Max. service temperature - Short term 　 ℃ 120 - 120 90 140 100 160 180 180 - 150 150 260 - 170 170 - - 130 155 300 310 310 270 260 260 220 200 180 360 - 140
Max. Service Temperature - Long term 　 ℃ 90 - 90 90 100 75 100 105 100 105 80 150 260 285 115 110 60 60 100 100 260 260 260 250 220 240 180 170 160 310 90 120
Thermal conductivity at 23 ℃ DIN 11359 W/(K*m) 0.42 0.40 0.41 0.42 0.30 0.17 0.23 0.23 - - 0.28 0.13 0.25 0.27 0.29 0.21 0.14 0.14 0.22 0.27 0.25 0.43 0.92 0.26 0.25 0.25 0.18 0.24 0.25 0.35 - 0.21
Coefficient of linear thermal expansion ISO 11359 10-4 * K-1 2.00 2.00 2.00 1.50 0.65 0.80 0.85 0.80 0.90 1.10 0.80 1.20 1.20 12.00 0.80 0.80 0.80 0.60 1.70 0.70 0.47 0.30 0.25 3.10 0.53 0.48 0.55 0.56 0.56 5.40 - 0.70
IV. Electrical Properties　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　
Dielectric constant at 1 MHz IEC 60250 106 Hz 3.00 - 2.90 2.35 - 3.30 3.50 3.70 - - 3.30 7.25 2.10 2.10 3.20 3.00 3.00 3.00 2.30 2.60 3.20 - - 3.90 3.20 4.10 3.50 2.90 3.00 3.55 - 3.00
Dielectric loss factor at 1 MHz IEC 60250 106 Hz 0.0001 - 0.0004 3.1 - 0.015 0.031 0.03 - - 0.02 0.18 0.0002 0.0002 0.014 0.012 0.01 0.01 0.0002 - 0.003 0.004 - 0.031 - 0.002 0.005 0.0013 0.006 0.0034 - 0.008
Volume resistivity IEC 60093 Ohm (Ω) * cm > 1014 < 106 > 1014 > 1016 109-11 ≧ 1015 ≧ 1013 ≧ 1015 - 1010-12 ≧ 1014 ≧ 1013 > 1016 > 1018 ≧ 1015 > 1013 ≧ 1015 ≧ 1015 ≧ 1016 ≧ 1014 ≧ 1016 ≧ 1013 > 105 > 1018 ≧ 1011 ≧ 1013 > 1016 ≧ 1013 ≧ 1013 ≧ 1014 - ≧ 1015
Surface resisivity IEC 60093 Ohm (Ω) > 1011 < 109 > 1011 > 1015 ≦ 1011 ≧ 1013 > 1012 ≧ 1013 - - ≧ 1013 ≧ 1014 > 1016 - ≧ 1014 > 1015 ≧ 1013 ≧ 1013 > 1013 ≧ 1013 ≧ 1015 ≧ 1013 - > 1018 ≧ 1015 ≧ 1015 > 1014 ≧ 1015 ≧ 1014 ≧ 1015 - ≧ 1015
Dielectric strength IEC 60243-1 kV/mm 45 45 40 17 - 22 50 50 - - 27 22 48 - 22 45 20 - 40 20 - 40 40 40 19 24.5 - 24 18 28 40 33 17 22 - -
V. Miscellaneous Data　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　
Flammability UL 94 Class HB HB HB HB HB HB HB HB HB HB HB V-0 V-0 HB HB HB V-0 V-0 HB HB V-0 V-0 V-0 V-0 V-0 V-0 V-0 V-0 V-0 V-0 HB HB
NOTE: 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m

Statement:
The information mentioned the above are approximate figures based on our experience & knowledge .
They are as HiShiRon® products and possible application.
HiShiRon® will not provide any legally binding guarantee of certain properties, or any suitablility.
What will you have in "Stock Shape"?
As the one of leading manufacturer of engineering plastic in Taiwan, Hishiron specializes in supplying semi-finished products in various kinds of plastic materials in the most popular shapes & sizes. In "Stock Shape", you will soon have access to the full dimension list. Material: UHMW PE (PE1000), HDPE, PP, POM (ACETAL), ABS, NYLON 6A, MC NYLON, PVC, PVDF, PTFE (TEFLON®), PETP, PEEK, PAI (TORLON), PEI (ULTEM), PPS..., etc.

Please contact us right now & tell us what you demand, Hishiron always glad to serve you by our rich experiences in engineering plastics.
Contact Us